Pend SHORE A POLYURETHANES
8 Dedicated to QUALITY, SERVICE, SAFETY, and INNOVATION
ENTERPRISES
An ISO-9001 Certified company
FP-90 REV 1 A/B a
90 SHORE A POLYURETHANE ELASTOMER
RoHS
BJB s FP (Fast Production) Series of products range from a 15 to 90 Shore A. You’ll find their 4 to 5 minute work time can easily be
demolded, tack free and tough in under an hour. The 1:2 ratio and low viscosity makes these translucent materials easy to mix, pour
and pigment. FP-90 REV | is ideal for hand casting or dispensed with our CPE equipment.
* RoHS/REACH Compliant Demold in under an hour Translucent and easy to pigment
4-5 minute work time * Low viscosity and easy to mix . a ideal for dispense
PHYSICAL PROPERTIES ELEVATED TEMPERATURE CURE*
Hardness, Shore A 9045
Density (alo) 1.097
Cubic Inches per Pound 26.03
Color/Appearance Clear Amber
Tensile Strength (psi) 2,250
Tensile Modulus (psi) 4,000
Elongation (%) 430
Tear Strength (pi) 240
Shrinkage (in/in) linear 0.0046*
Dielectric Constant, 1 MHz 4.704
Dissipation Factor, 1 MHz 0.0435
*Note: Reported physical properties are based on test specimens cured 2 hours at room temperature then 16 hours at 160 F (71 C).
*Shrink test specimens are cured for 24 hours at room temperature and then 16 hours at 160 F (71 C).
HANDLING PROPERTIES [ee PatA a] Part B
Mix Ratio by weight 100
Mix Ratio by volume [| tid 100
Specific Gravity @ 77 F (25 C) 1.039
Color Amber
Viscosity (cps) @ 77 F (25 C) Brookfield 870
Mixed Viscosity (cps) @ 77 F (25 C) Brookfield 1,500
Work Time, 100g mass @ 77 F (25 C) 4- 4.5 minutes
Gel Time 5 5.5 minutes
Demold Time @ 77 F (25 C) 60 90 minutes
Properties above are typical and not for specifications.
FP-90 A/B REV | Page | of 2 Date: 07/15/2022
For more information call BJB Enterprises, Inc. (714) 734-8450 Fax (714) 734-8929