EPOXY PRODUCTS (SYS) | Revchem Composites

81XR29A-2_TDS.pdf

Sat, 27 Sep 2025 10:31:02 +0000

Property Standard Units
100g Pot Life – minutes
Viscosity Mixed ASTM D2196 cP
Method Resin:Hardener
COMBINED FEATURES Weight 3.70:1
Volume 3.13:1
2024 Gougeon Brothers, Inc.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 7 / Mar 2024
100:32.0
100:27.0
FIRE RETARDANT LAMINATING
EPOXY
MIX RATIO
Resin:Hardener
HANDLING PROPERTIES
Technical Data
72 F (22 C)
135-165
720
Low viscosity for quick wet out of synthetic
composite fabrics; especially effective with Kevlar
and carbon fiber.
Medium speed hardenerprovides up to 150 minutes
of pot life at 72 F (22 C).
Fire retardant system contains high levels of
phosphorous to reduce flame spread and smoke
generation in a composite laminate when compared
to a standard resin system.
Optimizedfor hand wet out and machine
impregnation in contact molding, vacuum bagging and
filament winding applications.
Room temperature cure properties suitable for many
composite components and structures.
T
gas high as 138 F (59 C) with proper post cure
providing excellent temperature stability and great part
cosmetics.
XR29A~M2044
Caution-Stir Resin thoroughly with mechanical mixer
before blending with Hardener. Contents may settle
during storage.

116 (47) 118 (48)
138 (59)
121 (49) 119 (48)
THERMAL PROPERTIES
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
3.62E+05(2.5) 3.91E+05(2.7)
11,800(81) 12,900(89)
2.7 3.0
4.06E+05(2.8) 4.14E+05(2.85)
6,680(46) 7,390(51)
(81) 12,300(85)
83 84
11,800
Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
XR29A~M2044
FIRE RETARDANT LAMINATING EPOXY
MECHANICAL PROPERTIES
Property
S helf Li fe
Ye a r
3
Re s in
Ye a r
2
Har dene r
QC Tinting Availa

81XR28A-4_TDS.pdf

Sat, 27 Sep 2025 10:31:00 +0000

Distributed By
; Est @)ve2
PRO-SET. Piibarglass Sualy
. HANDLING PROPERTIES mil
Technical Data Property Standard) Units. 1-072″F (22 C)
100g Pot Life | ASTM 02471 | minutes | 225-275
XR28 A~M2046 _vicosivixes TASTMD2196| cP 325
Viscosity (resin) _ASTM D2196| cP | 480
FIRE RETARDANT | Viscosity (hardener) | ASTMD2196| cP | 115
INFUSION EPOXY
COMBINED FEATURES MIX RATIO DENSITY
Very low viscosity for rapid saturation of Method RosiniHardener: Resin:Hardener. State Units: 72 F (22 C)
fiberglass, Kevlar and carbon fiber Weight | 3.85:1 | 100:26.0 Resin | Ib/gal (g/cc) | 9.51 (1.14) |
laminate with resin infusion and VARTM Volume 3.23:1 I 100:31.0 Hardener | Ib/gal (g/cc) | 8.10 (0.97)
Processes. MECHANICAL PROPERTIES
js RT Gelation
Slow speed hardener provides about 4 Property Standard Units + 140 F (60 C)
hours of pot life at 72 F (22 C). xB hrs
Fire retardant syst ntains high Hardness | ASTM D2240 | Type D_| 54
EPOXIES for levels of phospherous to reduce flome Compression Vield “ASTM D695 psi (MPa) | 40,430 (72)
, et rn Tensile Strength __ASTM D638 | psi (MPa) | 8,040 (55)
Laminating spread and smoke generation in a Tensi + 7
i . ensile Modulus __ ASTM D638 psi (MPa) | 4.14E+05 (2854)
composite laminate when compared to a – . t – a 1 –
Infusion standard resin system Tensile Elongation | ASTM DES: e __| ae –
~ y’ . Flexural Strength | ASTM D790 | psi (MPa) | 14,000 (97)
Tooling This combination is formulated Flexural Modulus ASTMD790 | psi(MPa) | 4.27E+05 (2944)
: specifically for resin infusion and VARTM
Assembly processes. Do not use in open mold THERMAL PROPERTIES
icati RT Gelation
applications.
. | Property Standard Units + 140 F (60 C)
Elevated temperature cure is required. x 8 hrs
fougeon Brothers, Ino. |_ Tg DSC Onset-tst Heat |_ASTME1356 | F ( C) 127 (53)
P.0, Box 908 Heat Deflection Temperature | ASTM D648 SFC) | 124 (51
Bay City, Ml 48707 Ultimate Tg by DSC ASTM E1356 F( C) | 149 (65)”
prosetepoxy.com Additional post cure may be required; contact Technical Department for detail.
888-377.6738 ? Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many high-performance
~ ore epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this occurs, warm the resin to 125* F and stir
to dissolve crystals, Hardeners may form carbamation when exposed to CO, and moisture in the atmosphere for extended periods of time, Prevent
5090012018 Contitied carbamation by protecting hardeners from exposure unti immediately prior to processing.
Test specimens were neat f $)
epoxy (without fiber {
Rev 6 / Mar 2024 memnens 6
Typical values, not to be : can ~ QC Tinting Avaita
2024 Gougeon Brothers, Inc construed as specification. oe
To view more PRO-SET products, give us a visit at
fiberglasssupply.com!

81XR28A-2_TDS.pdf

Sat, 27 Sep 2025 10:30:59 +0000

Method State
Weight Resin
Volume Hardener
Hardness
Compression Yield 10,430
Tensile Strength 8,040
Tensile Modulus 4.14E+05
Tensile Elongation
Flexural Strength 14,000
Flexural Modulus 4.27E+05
Tg DSC Onset 1st Heat 127(53)
124(51)
149(65)
2024 Gougeon Brothers, Inc.
Rev 6 / Mar 2024
Ultimate Tg by DSC ASTM E1356 F ( C)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many high-performance
epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this occurs, warm the resin to 125 F and stir
to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture in the atmosphere for extended periods of time. Prevent
carbamation by protecting hardeners from exposure until immediately prior to processing.
Test specimens were neat
epoxy (without fiber
reinforcement).
Typical values, not to be
construed as specification.
ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
ASTM D790 psi (MPa) (2944)
THERMAL PROPERTIES
Property Standard Units
RT Gelation
+ 140 F (60 C)
x 8 hrs
ASTM D638 % 3.9
ASTM D790 psi (MPa) (97)
ASTM D638 psi (MPa) (55)
ASTM D638 psi (MPa) (2854)
ASTM D2240 Type D 84
ASTM D695 psi (MPa) (72)
3.23:1 100:31.0 lb/gal (g/cc)8.10 (0.97)
MECHANICAL PROPERTIES
Property Standard Units
RT Gelation
+ 140 F (60 C)
x 8 hrs
DENSITY
Resin:HardenerResin:Hardener Units 72 F (22 C)
3.85:1 100:26.0 lb/gal (g/cc)9.51 (1.14)
Viscosity (resin) ASTM D2196 cP 480
Viscosity (hardener)ASTM D2196 cP 115
MIX RATIO
100g Pot Life ASTM D2471minutes 225-275
Viscosity Mixed ASTM D2196 cP 325
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
XR28A~M2046
FIRE RETARDANT
INFUSION EPOXY
COMBINED FEATURES
Very low v iscosity for rapi d saturation of
fiberglass, K evlar and carbon fiber
laminate with resin infusion and VARTM
processes.
Slow sp eed hardener provides about 4
hours of pot lif e at 72 F (22 C).
Fire retardant system contains hi gh
levels of phosphorous t o reduce flame
spread and smok e generation in a
composite laminate when compared to a
standard resin system.
This combinati on is formulated
specifically for r esin infusion and VARTM
processes. Do not use in open mold
applications.
Elevated temperatur e cure is required.
S he lf L i fe
Ye a r
3
Re s in
Ye a r
2
Har dene r
QC Tinting Availa
To view more PRO-SET products, give us a visit at
fiberglasssupply.com!

81TLG625R2_TDS.pdf

Sat, 27 Sep 2025 10:30:57 +0000

PRO-SET.
. HANDLING PROPERTIES
Technical Data Property, Standardl)svsr/sUnitsiny, 65 F (18 C)))) 72 F (22 C) 85 F (29 C)
TLG – 62 5- R 100 mi Pot Life ASTM D2471 76-94 31-39 27-33 |
500 mi Pot Life ASTM D2471_| minutes | 54-66 | 27-38 24-30
TLG 62 5 H Viscosity (Mixed) ASTM 02196 cP Paste Paste Paste |
– –
MIX RATIO DENSITY
FAI RI NG PUTTY EPOXY Method Resin:Hardener): Resin;Hardener State Units 72 F (22 C)
Weight | 1791 | 100:55.9 | Mixed Ib/gal (g/cc) | 5.26 (.64) |
[he New COMBINED FEATURES Volume ti 100:100
Standard Low density epoxy fairing putty is designed ~ _app1 iGATION PROPERTIES
for filling and fairing applications in custom Property ieTemperature Units Tavalule
building or repair situations. 5
Cure time to sand in .25″ thickness T2 F (21 C) hours _| B.
Pre-thickened system to allow for easier | 90 F (32 c) hours 4
mixing and smooth spreading. It is not
DAVINEG fry Mecessary to add fillers to this combination. MECHANICAL PROPERTIES
EPOXIES for : ; Property. ju Standard Units 77 F.(25 C) X:2 WK
oo Medium cure speed hardener provides Hardness. | ASTM 02240 Type D 62
Laminating approximately 90 minutes of working time at Compression Yield ~~~ ~ ASTMD695 | psi(MPa) | 3,334 (23) |
: 72 F (22 C). a
ated Coverage one mixed gallon covers 6.4 THERMAL PROPERTIES
i . . Property | Standard: Units THF (25 C) x2 wk
Tooling square feet at 0.25″ thickness. Heat Deflection Temperature PASTMET357 | F ( C) W747)
Assembly Low shrinkage epoxy chemistry allows for
y applications up to 0.50″ thick. Additional MIXING RECOMMENDATIONS
application necessary to fill deeper voids. Mixing of Fairing Putty Epoxy requires a folding motion on a flat surface due to
cougeon Bretvers Easy to sand low density epoxy can easily be ire pasterlike consistency. If red by rand, alow 10 minute inatiction sme for
eon Braliets. he sanded to achieve a desired contour. thixotropic recovery before application. Ensure there are no streaks of color
Ee aes a8 when applying, this is a sign of inadequate mixing. Mix only as much as can be
Say City, M148/07 Room temperature cure properties suitable applied within the pot life of the mixture.
ik i 7: on for many composite plugs and molds Some separation may occur during storage. Stir resin and hardener individually
Cost effective, high performance Epoxy
soonon2015 ceniey formulation for synthetic composite ” Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
ae manufacturing. high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO and
Rev 2/Dec 2015 Shelf life is 18 months for resin and 18 moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
months for hardener when properly stored . immediately prior to processing.
2018 Gougeon Brothers, Ine Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.

81TLG625R1_TDS.pdf

Sat, 27 Sep 2025 10:30:56 +0000

81TLG625H2_TDS.pdf

Sat, 27 Sep 2025 10:30:55 +0000

81TLG625H1_TDS.pdf

Sat, 27 Sep 2025 10:30:54 +0000

81MGSR937D_TDS.pdf

Sat, 27 Sep 2025 10:30:53 +0000

2
.. HEXION
Responsible Chemistry
EPIKO and EPIKURE Curing Agent MGS RIMH
Application
Low viscous infusion resin system for processing of woven and non-crimp multiaxial fabrics of low to high areal weight. Due to its very good
mechanical properties, this system is suitable for the production of components featuring high static and dynamic loadability and high heat
resistance.
Infusion resin RIMR 935 is based on bisphenol AF resin. Hardener RIMH 936 and RIMH 937 are a modification of aliphatic and cycloaliphatic
amines. Pot life (100 g mixed at 30 *C/86 F) is approximately 2 hours for RIMH 936 and 3,5 h for RIMH 937. Optimum viscosities for infusion are
tealized at temperatures in the range of 25 – 35 C (77 – 95 F). Pot life is then between approx. 1h (RIMH 936 at 40 C/104 F) to 5 h (RIMH 937
at 25 C/77 F). Following initial curing at room temperature, the parts are still brittle and require heat treatment at a min. temperature of 50
*C/122 F before processing or demoulding. Direct curing at elevated temperatures (60 C-100 C/140 *F-212 F) is possible. The curing time can
be reduced to a few minutes by this.
Non-tacky, high-gloss surfaces are obtained even with unfavourable curing conditions, such as low temperatures or high relative humidity.
The infusion resin system does not contain any unreactive components. All raw materials and additives feature a very low vapor pressure,
therefore permitting processing of the material under vacuum even at elevated temperatures. Compatibility problems are not to be expected in
combination with suitable geicoats, various paints (e.g., PUR-based), etc., however comprehensive tests are indispensable
These products can be stored for at least 24 months in their carefully sealed original containers. Even though it is unlikely, these products may
crystallise at temperatures below +15 C. The crystallisation is visible as a clouding or solidification of the contents of the container. If
crystallisation of either component should be observed, it can removed by warming up. Slow warming up to approx. 50 C-60 C (122 *F-140 F) in
a water bath or oven and stirring or shaking will clarify the contents of the container without any loss of quality. Use only completely transparent
products. Before warming up, open containers slightly to permit equalization of pressure. Caution during warm-up! Do not warm up over an open
flame! While stirring up, use safety equipment (gloves, eyeglasses, respirator equipment).
The relevant industrial safety regulations for the handling of epoxy resins and hardeners and our instructions for safe processing are to be
observed.
Specifications
Resin RIMR 935,
Density ig/om?} 4,14 – 1,20
Viscosity [mPas] 400 – 800
Epoxy equivalent [g/equivalent] 155 – 165
Epoxy value [equivalent/100g) 0,61 – 0,64
Refractory index 1,5350 – 15450
Hardener RIMH 936 Hardener RIMH 937
Density [glom?} 0,92 – 0,97 0,92 – 0,96
Viscosity [mPas] 10-50 30 – 100
Amine Value {mg KOH/g] 550 – 650 450 – 500
Refractory index 1,4850 – 1,4920 1,4920 – 1,5020
Measuring conditions: measured at 25 C / 77 F
EPIKOTE Resin MGS RIMR 935 and EPIKURE Ouring Agent MGS RIMH 936 – 937 Generated. October 23, 2020
saue Dole
The infosmation provided herein wast . rate at tie time of preparation or prepared from sourmes believed (o be reliable, butit isthe respensbillty of
the user to invesicate and understand city i $s Hic compty with all (ews and procedures applicable 1o the safe handlina and use of the product and to deterring

81M2044-4_TDS.pdf

Sat, 27 Sep 2025 10:30:52 +0000

Property Standard Units
100g Pot Life ASTM D2471Minutes
500g Pot Life ASTM D2471Minutes
Viscosity MixedASTM D2196 cP
Viscosity (resin)ASTM D2196 cP
Viscosity (hardener)ASTM D2196 cP
COMBINED FEATURES Method Resin:Hardener
Weight 3.34:1
Weight Range 3.17:1 3.73:1
Volume 2.84:1
Volume Range 2.70:1 3.18:1
State Units 72 F (22 C)
Cured lb/gal (g/cc)9.3 (1.11)
Resin lb/gal (g/cc)9.47 (1.14)
Hardener lb/gal (g/cc)8.07 (0.97)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
72 F (22 C)
69-85
54-66
450
1,200
LAMINATING EPOXY
70
MIX RATIO
Resin:Hardener
100:30.0
100:31.5 100:26.8
100:37.0 100:31.5
100:35.2
DENSITY
Rev 2 /Dec 2015 Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Low viscosity for good wet out of all
synthetic composite fabrics and core
materials.

Slow cure hardener provides approximately
160 minutes of working time at 72 F (22 C). A
typical laminate will gel in about 4 to 5 hours
at 72 F (22 C).

Optimized for hand wet out and machine
impregnation in contact molding, vacuum
bagging and filament winding applications.

Room temperature cure properties suitable
for many composite components and
structures.

T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.
M1040~M2044

Hardness ASTM D2240Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790psi (GPa)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Tg DSC Ultimate ASTM E1356 F ( C)
Rev 2 /Dec 2015
2015 Gougeon Brothers, Inc.
M1040~M2044
LAMINATING EPOXY
MECHANICAL PROPERTIES
RT Gelation
+ 180 F (82 C)
x 4 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
80 80 80 80
Property Standard Units
72 F (22 C)
x 2wk
RT Gelation
+ 110 F
(43 C)
RT Gelation
+ 140 F (60 C)
x 8 hrs
81
14,500(100) 14,600(101) 14,700(101) 13,500(93) 14,900(103)
7,550(52) 9,780(67) 10,200(70) 9,720(67) 9,980(69)
5.10E+05(3.52)4.48E+05(3.09)4.47E+05(3.08)4.15E+05(2.86)4.22E+05(2.91)
3.5 4.0 4.1 4.4 4.0
(3.42)5.15E+05(3.55)
(121) 16,500(114) 17,500(121)
5.10E+05(3.52)5.11E+05(3.52)
13,000(90) 17,100(118) 17,600
THERMAL PROPERTIES
Property Standard Units
72 F (22 C)
x 2wk
5.08E+05(3.5) 4.96E+05
RT Gelation
+ 110 F
(43 C)
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 4 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
133 (56) 137 (58) 148 (64) 158 (70) 161 (72)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many high-performance
epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this occurs, warm the resin to 125 F
and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture in the atmosphere for extended periods of time.
Prevent carbamation by protecting hardeners from exposure until immediately prior to processing.
122 (50) 131 (55) 143 (62) 143 (62) 157 (69)
172 (78)

81MGSR935D_TDS.pdf

Sat, 27 Sep 2025 10:30:52 +0000

81M2044-1_TDS.pdf

Sat, 27 Sep 2025 10:30:50 +0000

Slow cure hardener provides approximately
160 minutes of working time at 72 F (22 C). A
typical laminate will gel in about 4 to 5 hours
at 72 F (22 C).

Optimized for hand wet out and machine
impregnation in contact molding, vacuum
bagging and filament winding applications.

Room temperature cure properties suitable
for many composite components and
structures.

T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.
M1040~M2044

81M2044-2_TDS.pdf

Sat, 27 Sep 2025 10:30:50 +0000

Slow cure hardener provides approximately
160 minutes of working time at 72 F (22 C). A
typical laminate will gel in about 4 to 5 hours
at 72 F (22 C).

Optimized for hand wet out and machine
impregnation in contact molding, vacuum
bagging and filament winding applications.

Room temperature cure properties suitable
for many composite components and
structures.

T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.
M1040~M2044

81M1040-4_TDS.pdf

Sat, 27 Sep 2025 10:30:49 +0000

Slow cure hardener provides approximately
160 minutes of working time at 72 F (22 C). A
typical laminate will gel in about 4 to 5 hours
at 72 F (22 C).

Optimized for hand wet out and machine
impregnation in contact molding, vacuum
bagging and filament winding applications.

Room temperature cure properties suitable
for many composite components and
structures.

T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.
M1040~M2044

81M1040-1_TDS.pdf

Sat, 27 Sep 2025 10:30:47 +0000

Slow cure hardener provides approximately
160 minutes of working time at 72 F (22 C). A
typical laminate will gel in about 4 to 5 hours
at 72 F (22 C).

Optimized for hand wet out and machine
impregnation in contact molding, vacuum
bagging and filament winding applications.

Room temperature cure properties suitable
for many composite components and
structures.

T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.
M1040~M2044

81M1040-2_TDS.pdf

Sat, 27 Sep 2025 10:30:47 +0000

Slow cure hardener provides approximately
160 minutes of working time at 72 F (22 C). A
typical laminate will gel in about 4 to 5 hours
at 72 F (22 C).

Optimized for hand wet out and machine
impregnation in contact molding, vacuum
bagging and filament winding applications.

Room temperature cure properties suitable
for many composite components and
structures.

T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.
M1040~M2044

81M10020-G_TDS.pdf

Sat, 27 Sep 2025 10:30:45 +0000

Property Standard Units
100g Pot Life ASTM D2471minutes
Viscosity MixedASTM D2196 cP
Viscosity (resin)ASTM D2196 cP
Viscosity (hardener)ASTM D2196 cP
Method Resin:Hardener
COMBINED FEATURES Weight 4.0:1
Weight Range 3.78:1 4.46:1
Volume 3.70:1
Volume Range 3.52:1 4.15:1
State Units 72 F (22 C)
Cured lb/gal (g/cc)9.8 (1.17)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
72 F (22 C)
15-19
2775
4,800
2,400
TOUGHENED LAMINATING EPOXY
MIX RATIO
100:25.0
Resin:Hardener
26.40:1 22.40:1
100:27.0
28.40:1 24.10:1
DENSITY
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4/ Dec 2015
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Extra Fast cure speed hardener provides a 25
minute working time at 72 F (22 C). A typical
laminate will be gelled in about 1 to 2 hours.

Room temperature cure properties suitable for
many composite components and structures.

T
g as high as 162 F (72 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.

M1002
M2015

Hardness ASTM D2240Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790psi (GPa)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Tg DSC Ultimate ASTM E1356 F ( C)
Rev 4/ Dec 2015
2015 Gougeon Brothers, Inc.
M1002~M2015
TOUGHENED LAMINATING EPOXY
MECHANICAL PROPERTIES
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
82 83 83 84 84
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 110 F (43 C)
x 8 hrs
RT Gelation
+ 125 F (52 C)
x 8 hrs
13,290(92) 13,800(95)
8,490(59) 8,670(60) 9,280(64) 10,000(69) 9,250(64)
14,000(97) 14,200(98) 13,600(94)
(3.12)4.80E+00(.) 4.53E+05(3.12)
4.2 3.9 3.9 4.1
4.68E+05(3.23)4.54E+05(3.13)4.52E+05
4.3
14,800(102) 15,819(109) 15,600(108) 15,700(108) 15,500(107)
4.64E+05(3.2) 4.53E+05(3.12)4.52E+05(3.12)4.49E+05(3.1) 4.53E+05(3.12)
THERMAL PROPERTIES
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 110 F (43 C)
x 8 hrs
RT Gelation
+ 125 F (52 C)
x 8 hrs
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
130 (54) 143 (62) 141 (61) 151 (66) 153 (67)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately prior
to processing.
129 (54) 142 (61) 148 (64) 152 (67) 155 (68)
162 (72)

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 175
Heat Deflection Temperature F ( C) 166
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 40
100g Pot Life ASTM D2471 minutes 123-151
Viscosity Mixed ASTM D2196 cP 1,600
3.33:1 3.00:1 3.76:1 100:30.0 100:33.30 100:26.60
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.73:1 4.65:1 100:24.0 100:26.80 100:21.50
Property Standard Units
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 82 83
ASTM D695 psi (MPa)13,900(96) 13,800(95)
ASTM D638 psi (MPa)4.29E+05(2.96)3.86E+05(2.66)
ASTM D638 psi (MPa) 9,722(67) 9,500(66)
ASTM D638 % 4.5 6.4
ASTM D790 psi (MPa)18,500(128) 17,500(121)
THERMAL PROPERTIES
Property StandardUnits
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
ASTM D790 psi (MPa)5.56E+05(3.83)5.07E+05(3.5)
Ultimate Tg by DSC ASTM E1356 193(89)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately
prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (79) 193(89)
ASTM D648 (74) 184(84)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Extra Slow cure speed hardener provides 6 to
8 hours of working time at 72 F (22 C).

Elevated temperature cure is required;
thermal and mechanical properties suitable for
composite components and high temperature
tooling and molds.

T
g as high as 193 F (89 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 18 months for
hardener when properly stored
2
.

M1002
M2042

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 128
Heat Deflection Temperature F ( C) 125
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 180
100g Pot Life ASTM D2471 minutes 25-31
Viscosity Mixed ASTM D2196 cP 2,200
3.57:1 3.46:1 4.07:1 100:28.0 100:28.90 100:24.60
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 4.07:1 4.78:1 100:24.0 100:24.60 100:20.90
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 82 83
ASTM D695 psi (MPa)13,800(95) 14,600(101)
ASTM D638 psi (MPa)4.86E+05(3.35)4.59E+05(3.16)
ASTM D638 psi (MPa) 7,160(49) 9,600(66)
ASTM D638 % 2.0 3.4
ASTM D790 psi (MPa)12,500(86) 18,300(126)
THERMAL PROPERTIES
Property StandardUnits
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
ASTM D790 psi (MPa)4.72E+05(3.25)5.96E+05(4.11)
Ultimate Tg by DSC ASTM E1356 172(78)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately
prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (53) 161(72)
ASTM D648 (52) 159(71)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Fast cure speed hardener provides 1.5 to 2.5
hours of working time at 72 F (22 C).

Room temperature cure properties suitable for
many composite components and structures.

T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.

M1002
M2043

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 127
Heat Deflection Temperature F ( C) 124
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 75
100g Pot Life ASTM D2471 minutes 48-60
Viscosity Mixed ASTM D2196 cP 1,400
3.45:1 3.25:1 3.82:1 100:29.0 100:30.80 100:26.20
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.91:1 4.61:1 100:24.0 100:25.60 100:21.70
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 80 84
ASTM D695 psi (MPa)13,600(94) 14,100(97)
ASTM D638 psi (MPa)4.76E+05(3.28)4.52E+05(3.12)
ASTM D638 psi (MPa) 7,550(52) 9,690(67)
ASTM D638 % 2.1 4.0
ASTM D790 psi (MPa)12,400(85) 14,100(97)
THERMAL PROPERTIES
Property StandardUnits
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
ASTM D790 psi (MPa)4.73E+05(3.26)5.99E+05(4.13)
Ultimate Tg by DSC ASTM E1356 162(72)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (53) 153(67)
ASTM D648 (51) 162(72)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Medium cure speed hardener provides 2.5 to
4.5 hours of working time at 72 F (22 C).

Room temperature cure properties suitable for
many composite components and structures.

T
g as high as 162 F (72 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.

M1002
M2044

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 176
Heat Deflection Temperature F ( C) 170
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 115
100g Pot Life ASTM D2471 minutes 72-88
Viscosity Mixed ASTM D2196 cP 2,100
3.57:1 3.16:1 3.95:1 100:28.0 100:31.60 100:25.30
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.83:1 4.78:1 100:24.0 100:26.10 100:20.90
Property Standard Units
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 83 83
ASTM D695 psi (MPa)14,100(97) 13,900(96)
ASTM D638 psi (MPa)4.33E+05(2.99)3.94E+05(2.72)
ASTM D638 psi (MPa)10,000(69) 9,590(66)
ASTM D638 % 5.5 5.7
ASTM D790 psi (MPa)18,800(130) 1,770(12)
THERMAL PROPERTIES
Property StandardUnits
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
ASTM D790 psi (MPa)5.55E+05(3.83)5.14E+05(3.54)
Ultimate Tg by DSC ASTM E1356 197(92)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (80) 197(92)
ASTM D648 (77) 189(87)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Slow cure speed hardener provides 4.5 to 6
hours of working time at 72 F (22 C).

Elevated temperature cure is required;
thermal and mechanical properties suitable for
composite components and high temperature
tooling and molds.

T
g as high as 197 F (92 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 18 months for
hardener when properly stored
2
.

M1002
M2046

81M1002-2_TDS.pdf

Sat, 27 Sep 2025 10:30:43 +0000

Extra Fast cure speed hardener provides a 25
minute working time at 72 F (22 C). A typical
laminate will be gelled in about 1 to 2 hours.

Room temperature cure properties suitable for
many composite components and structures.

T
g as high as 162 F (72 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.

M1002
M2015

Hardness ASTM D2240Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790psi (GPa)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Tg DSC Ultimate ASTM E1356 F ( C)
Rev 4/ Dec 2015
2015 Gougeon Brothers, Inc.
M1002~M2015
TOUGHENED LAMINATING EPOXY
MECHANICAL PROPERTIES
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
82 83 83 84 84
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 110 F (43 C)
x 8 hrs
RT Gelation
+ 125 F (52 C)
x 8 hrs
13,290(92) 13,800(95)
8,490(59) 8,670(60) 9,280(64) 10,000(69) 9,250(64)
14,000(97) 14,200(98) 13,600(94)
(3.12)4.80E+00(.) 4.53E+05(3.12)
4.2 3.9 3.9 4.1
4.68E+05(3.23)4.54E+05(3.13)4.52E+05
4.3
14,800(102) 15,819(109) 15,600(108) 15,700(108) 15,500(107)
4.64E+05(3.2) 4.53E+05(3.12)4.52E+05(3.12)4.49E+05(3.1) 4.53E+05(3.12)
THERMAL PROPERTIES
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 110 F (43 C)
x 8 hrs
RT Gelation
+ 125 F (52 C)
x 8 hrs
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
130 (54) 143 (62) 141 (61) 151 (66) 153 (67)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately prior
to processing.
129 (54) 142 (61) 148 (64) 152 (67) 155 (68)
162 (72)

Extra Slow cure speed hardener provides 6 to
8 hours of working time at 72 F (22 C).

Elevated temperature cure is required;
thermal and mechanical properties suitable for
composite components and high temperature
tooling and molds.

T
g as high as 193 F (89 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 18 months for
hardener when properly stored
2
.

M1002
M2042

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 128
Heat Deflection Temperature F ( C) 125
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 180
100g Pot Life ASTM D2471 minutes 25-31
Viscosity Mixed ASTM D2196 cP 2,200
3.57:1 3.46:1 4.07:1 100:28.0 100:28.90 100:24.60
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 4.07:1 4.78:1 100:24.0 100:24.60 100:20.90
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 82 83
ASTM D695 psi (MPa)13,800(95) 14,600(101)
ASTM D638 psi (MPa)4.86E+05(3.35)4.59E+05(3.16)
ASTM D638 psi (MPa) 7,160(49) 9,600(66)
ASTM D638 % 2.0 3.4
ASTM D790 psi (MPa)12,500(86) 18,300(126)
THERMAL PROPERTIES
Property StandardUnits
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
ASTM D790 psi (MPa)4.72E+05(3.25)5.96E+05(4.11)
Ultimate Tg by DSC ASTM E1356 172(78)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately
prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (53) 161(72)
ASTM D648 (52) 159(71)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Fast cure speed hardener provides 1.5 to 2.5
hours of working time at 72 F (22 C).

Room temperature cure properties suitable for
many composite components and structures.

T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.

M1002
M2043

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 127
Heat Deflection Temperature F ( C) 124
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 75
100g Pot Life ASTM D2471 minutes 48-60
Viscosity Mixed ASTM D2196 cP 1,400
3.45:1 3.25:1 3.82:1 100:29.0 100:30.80 100:26.20
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.91:1 4.61:1 100:24.0 100:25.60 100:21.70
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 80 84
ASTM D695 psi (MPa)13,600(94) 14,100(97)
ASTM D638 psi (MPa)4.76E+05(3.28)4.52E+05(3.12)
ASTM D638 psi (MPa) 7,550(52) 9,690(67)
ASTM D638 % 2.1 4.0
ASTM D790 psi (MPa)12,400(85) 14,100(97)
THERMAL PROPERTIES
Property StandardUnits
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
ASTM D790 psi (MPa)4.73E+05(3.26)5.99E+05(4.13)
Ultimate Tg by DSC ASTM E1356 162(72)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (53) 153(67)
ASTM D648 (51) 162(72)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Medium cure speed hardener provides 2.5 to
4.5 hours of working time at 72 F (22 C).

Room temperature cure properties suitable for
many composite components and structures.

T
g as high as 162 F (72 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.

M1002
M2044

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 176
Heat Deflection Temperature F ( C) 170
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 115
100g Pot Life ASTM D2471 minutes 72-88
Viscosity Mixed ASTM D2196 cP 2,100
3.57:1 3.16:1 3.95:1 100:28.0 100:31.60 100:25.30
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.83:1 4.78:1 100:24.0 100:26.10 100:20.90
Property Standard Units
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 83 83
ASTM D695 psi (MPa)14,100(97) 13,900(96)
ASTM D638 psi (MPa)4.33E+05(2.99)3.94E+05(2.72)
ASTM D638 psi (MPa)10,000(69) 9,590(66)
ASTM D638 % 5.5 5.7
ASTM D790 psi (MPa)18,800(130) 1,770(12)
THERMAL PROPERTIES
Property StandardUnits
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
ASTM D790 psi (MPa)5.55E+05(3.83)5.14E+05(3.54)
Ultimate Tg by DSC ASTM E1356 197(92)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (80) 197(92)
ASTM D648 (77) 189(87)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Slow cure speed hardener provides 4.5 to 6
hours of working time at 72 F (22 C).

Elevated temperature cure is required;
thermal and mechanical properties suitable for
composite components and high temperature
tooling and molds.

T
g as high as 197 F (92 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 18 months for
hardener when properly stored
2
.

M1002
M2046

81M1002-1_TDS.pdf

Sat, 27 Sep 2025 10:30:40 +0000

Extra Fast cure speed hardener provides a 25
minute working time at 72 F (22 C). A typical
laminate will be gelled in about 1 to 2 hours.

Room temperature cure properties suitable for
many composite components and structures.

T
g as high as 162 F (72 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.

M1002
M2015

Hardness ASTM D2240Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790psi (GPa)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Tg DSC Ultimate ASTM E1356 F ( C)
Rev 4/ Dec 2015
2015 Gougeon Brothers, Inc.
M1002~M2015
TOUGHENED LAMINATING EPOXY
MECHANICAL PROPERTIES
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
82 83 83 84 84
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 110 F (43 C)
x 8 hrs
RT Gelation
+ 125 F (52 C)
x 8 hrs
13,290(92) 13,800(95)
8,490(59) 8,670(60) 9,280(64) 10,000(69) 9,250(64)
14,000(97) 14,200(98) 13,600(94)
(3.12)4.80E+00(.) 4.53E+05(3.12)
4.2 3.9 3.9 4.1
4.68E+05(3.23)4.54E+05(3.13)4.52E+05
4.3
14,800(102) 15,819(109) 15,600(108) 15,700(108) 15,500(107)
4.64E+05(3.2) 4.53E+05(3.12)4.52E+05(3.12)4.49E+05(3.1) 4.53E+05(3.12)
THERMAL PROPERTIES
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 110 F (43 C)
x 8 hrs
RT Gelation
+ 125 F (52 C)
x 8 hrs
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
130 (54) 143 (62) 141 (61) 151 (66) 153 (67)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately prior
to processing.
129 (54) 142 (61) 148 (64) 152 (67) 155 (68)
162 (72)

Extra Slow cure speed hardener provides 6 to
8 hours of working time at 72 F (22 C).

Elevated temperature cure is required;
thermal and mechanical properties suitable for
composite components and high temperature
tooling and molds.

T
g as high as 193 F (89 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 18 months for
hardener when properly stored
2
.

M1002
M2042

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 128
Heat Deflection Temperature F ( C) 125
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 180
100g Pot Life ASTM D2471 minutes 25-31
Viscosity Mixed ASTM D2196 cP 2,200
3.57:1 3.46:1 4.07:1 100:28.0 100:28.90 100:24.60
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 4.07:1 4.78:1 100:24.0 100:24.60 100:20.90
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 82 83
ASTM D695 psi (MPa)13,800(95) 14,600(101)
ASTM D638 psi (MPa)4.86E+05(3.35)4.59E+05(3.16)
ASTM D638 psi (MPa) 7,160(49) 9,600(66)
ASTM D638 % 2.0 3.4
ASTM D790 psi (MPa)12,500(86) 18,300(126)
THERMAL PROPERTIES
Property StandardUnits
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
ASTM D790 psi (MPa)4.72E+05(3.25)5.96E+05(4.11)
Ultimate Tg by DSC ASTM E1356 172(78)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and moisture
in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until immediately
prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (53) 161(72)
ASTM D648 (52) 159(71)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Fast cure speed hardener provides 1.5 to 2.5
hours of working time at 72 F (22 C).

Room temperature cure properties suitable for
many composite components and structures.

T
g as high as 172 F (78 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.

M1002
M2043

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 127
Heat Deflection Temperature F ( C) 124
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 75
100g Pot Life ASTM D2471 minutes 48-60
Viscosity Mixed ASTM D2196 cP 1,400
3.45:1 3.25:1 3.82:1 100:29.0 100:30.80 100:26.20
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.91:1 4.61:1 100:24.0 100:25.60 100:21.70
Property Standard Units
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 80 84
ASTM D695 psi (MPa)13,600(94) 14,100(97)
ASTM D638 psi (MPa)4.76E+05(3.28)4.52E+05(3.12)
ASTM D638 psi (MPa) 7,550(52) 9,690(67)
ASTM D638 % 2.1 4.0
ASTM D790 psi (MPa)12,400(85) 14,100(97)
THERMAL PROPERTIES
Property StandardUnits
72 F (22 C)
x 2 wk
RT Gelation
+ 140 F (60 C)
x 8 hrs
ASTM D790 psi (MPa)4.73E+05(3.26)5.99E+05(4.13)
Ultimate Tg by DSC ASTM E1356 162(72)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (53) 153(67)
ASTM D648 (51) 162(72)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Medium cure speed hardener provides 2.5 to
4.5 hours of working time at 72 F (22 C).

Room temperature cure properties suitable for
many composite components and structures.

T
g as high as 162 F (72 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 2 years for
hardener when properly stored
2
.

M1002
M2044

Method
Weight
Volume
COMBINED FEATURES
State
Cured
Hardness
Compression Yield
Tensile Strength
Tensile Modulus
Tensile Elongation
Flexural Strength
Flexural Modulus
Tg DSC Onset 1st Heat F ( C) 176
Heat Deflection Temperature F ( C) 170
F ( C)
2015 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
Property Standard Units 72 F (22 C)
Viscosity (resin) ASTM D2196 cP 4,800
Viscosity (hardener)ASTM D2196 cP 115
100g Pot Life ASTM D2471 minutes 72-88
Viscosity Mixed ASTM D2196 cP 2,100
3.57:1 3.16:1 3.95:1 100:28.0 100:31.60 100:25.30
DENSITY
Units 72 F (22 C)
MIX RATIO
TOUGHENED LAMINATING EPOXY
Resin:Hardener Range Resin:Hardener Range
4.17:1 3.83:1 4.78:1 100:24.0 100:26.10 100:20.90
Property Standard Units
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
lb/gal (g/cc)9.81 (1.17)
MECHANICAL PROPERTIES
ASTM D2240 Type D 83 83
ASTM D695 psi (MPa)14,100(97) 13,900(96)
ASTM D638 psi (MPa)4.33E+05(2.99)3.94E+05(2.72)
ASTM D638 psi (MPa)10,000(69) 9,590(66)
ASTM D638 % 5.5 5.7
ASTM D790 psi (MPa)18,800(130) 1,770(12)
THERMAL PROPERTIES
Property StandardUnits
RT Gelation
+ 140 F (60 C)
x 8 hrs
RT Gelation
+ 180 F (82 C)
x 8 hrs
ASTM D790 psi (MPa)5.55E+05(3.83)5.14E+05(3.54)
Ultimate Tg by DSC ASTM E1356 197(92)
1
Additional post cure may be required; contact Technical Department for details.
2
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before use. As with many
high-performance epoxy resins, repeated exposure to low temperatures during storage may cause the resin to crystallize. If this
occurs, warm the resin to 125 F and stir to dissolve crystals. Hardeners may form carbamation when exposed to CO
2 and
moisture in the atmosphere for extended periods of time. Prevent carbamation by protecting hardeners from exposure until
immediately prior to processing.
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
Rev 4 / Dec 2015
Some separation may occur during storage. Stir resin before
mixing with hardener.
ASTM E1356 (80) 197(92)
ASTM D648 (77) 189(87)
Medium viscosity for good wet out of all
synthetic composite fabrics and core materials.

Slow cure speed hardener provides 4.5 to 6
hours of working time at 72 F (22 C).

Elevated temperature cure is required;
thermal and mechanical properties suitable for
composite components and high temperature
tooling and molds.

T
g as high as 197 F (92 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Cost effective, high performance epoxy
formulation for synthetic composite
manufacturing.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product code
on your order.

Shelf life is 3 years for resin and 18 months for
hardener when properly stored
2
.

M1002
M2046

81LAM251-5_TDS.pdf

Sat, 27 Sep 2025 10:30:38 +0000

Property Standard Units 77 F (25 C)85 F (29 C)
150g Pot Life ASTM D2471minutes 263-323 192-236
500g Pot Life ASTM D2471minutes 211-259 138-170
Viscosity MixedASTM D2196 cP 1508 1046
Viscosity (resin)ASTM D2196 cP
Viscosity (hardener)ASTM D2196 cP
COMBINED FEATURES Method Resin:Hardener
Weight 3.5:1
Weight Range 3.75:1 3.30:1
Volume 3.00:1
Volume Range 3.14:1 2.75:1
State Units 72 F (22 C)
Cured lb/gal (g/cc)9.45 (1.13)
Resin lb/gal (g/cc)9.69 (1.16)
Hardener lb/gal (g/cc)7.86 (0.94)
2018 Gougeon Brothers, Inc.
HANDLING PROPERTIES
Technical Data
72 F (22 C)
358-438
276-338
1885
6300
121
LAMINATING EPOXY MIX RATIO
Resin:Hardener
100:28.6
100:26.6 100:30.3
100:31.9 100:36.3
100:33.3
DENSITY
Rev 3 / Dec 2015
Test specimens were neat epoxy (without fiber reinforcement).
Typical values, not to be construed as specification.
VISCOSITY VS TEMPERATURE
High temperature, high performance epoxy
formulation for synthetic composite mold and
tooling manufacture.

T
g as high as 350 F (176 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Medium viscosity for wet out of synthetic
composite fabrics; especially effective with
carbon fiber.

Extra slow cure speed hardener provides 8
to 10 hours of working time at 77 F (25 C). A
typical laminate will be gelled in 14 to 20
hours at room temperature.

Optimized for hand wet out and machine
impregnation in contact molding, wet vacuum
bagging and Light RTM applications.

Elevated temperature cure is required;
thermal and mechanical properties suitable
for composite components and high
temperature tooling and molds.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.

Shelf life is 3 years for resin and 18 months
for hardener when properly stored
3
.
0
500
1000
1500
2000
2500
3000
3500
4000
4500
5000
50 60 70 80 90 100 110 120 130
Viscosity (cP)

Temperature ( F)
LAM-151-HT
LAM-251-HT

Hardness ASTM D2240Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790psi (GPa)
Tg DMA Peak Tan Delta ASTM E1640
1
F ( C)
Tg DMA Onset Storage ModulusASTM E1640
1
F ( C)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Tg DSC Ultimate ASTM E1356 F ( C)
Rev 3 / Dec 2015
2018 Gougeon Brothers, Inc.
LAM-151-HT~LAM-251-HT
LAMINATING EPOXY
MECHANICAL PROPERTIES
89 90 87 86
Property Standard Units
200 F (93 C)
x 12 hrs
250 F (121 C)
x 8 hrs
140 F (60 C) x 2 hrs
+ 302 F (150 C)
x 4 hrs
87
16,600(114) 16,700(115) 16,300(112) 13,500(93) 13,500(93)
12,500(86) 10,800(74) 9,240(64) 9,690(67) 9,690(67)
4.75E+05(3.28)4.56E+05(3.14)4.14E+05(2.85)4.68E+05(3.23)4.28E+05(2.95)
5.5 3.9 3.8 4.2 5.6
(3.45)4.82E+05(3.32)
(105) 17,600(121) 18,100(125)
4.43E+05(3.05)4.10E+05(2.83)
21,400(148) 18,800(130) 15,200
THERMAL PROPERTIES
Property Standard Units
200 F (93 C)
x 12 hrs
3.84E+05(2.65)5.01E+05
250 F (121 C)
x 8 hrs
140 F (60 C) x 2 hrs
+ 302 F (150 C)
x 4 hrs
281 (138) 303 (151) 357 (181) 193 (90) 195 (91)
346 (175)
1
1 Hz, 3 C per minute.
2
Additional post cure may be required; contact Technical Department for details.
3
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before
use. As with many high-performance epoxy resins, repeated exposure to low temperatures during storage
may cause the resin to crystallize. If this occurs, warm the resin to 125 F and stir to dissolve crystals.
Hardeners may form carbamation when exposed to CO
2 and moisture in the atmosphere for extended periods
of time. Prevent carbamation by protecting hardeners from exposure until immediately prior to processing.
172 (78)
251 (122) 282 (139) 324 (162) 153 (67) 173 (78)
250 (121) 286 (141) 328 (164) 170 (77) 190 (88)
252 (122) 277 (136) 339 (171) 157 (69)

81LAM251-4_TDS.pdf

Sat, 27 Sep 2025 10:30:36 +0000

T
g as high as 350 F (176 C) with proper post
cure providing excellent temperature stability
and great part cosmetics.

Medium viscosity for wet out of synthetic
composite fabrics; especially effective with
carbon fiber.

Extra slow cure speed hardener provides 8
to 10 hours of working time at 77 F (25 C). A
typical laminate will be gelled in 14 to 20
hours at room temperature.

Optimized for hand wet out and machine
impregnation in contact molding, wet vacuum
bagging and Light RTM applications.

Elevated temperature cure is required;
thermal and mechanical properties suitable
for composite components and high
temperature tooling and molds.

Quality-control tinting is available at no extra
charge; simply add “QC” after the product
code on your order.

Shelf life is 3 years for resin and 18 months
for hardener when properly stored
3
.
0
500
1000
1500
2000
2500
3000
3500
4000
4500
5000
50 60 70 80 90 100 110 120 130
Viscosity (cP)

Temperature ( F)
LAM-151-HT
LAM-251-HT

Hardness ASTM D2240Type D
Compression Yield ASTM D695psi (MPa)
Tensile Strength ASTM D638psi (MPa)
Tensile Modulus ASTM D638psi (GPa)
Tensile Elongation ASTM D638 %
Flexural Strength ASTM D790psi (MPa)
Flexural Modulus ASTM D790psi (GPa)
Tg DMA Peak Tan Delta ASTM E1640
1
F ( C)
Tg DMA Onset Storage ModulusASTM E1640
1
F ( C)
Tg DSC Onset 1st Heat ASTM E1356 F ( C)
Heat Deflection TemperatureASTM D648 F ( C)
Tg DSC Ultimate ASTM E1356 F ( C)
Rev 3 / Dec 2015
2018 Gougeon Brothers, Inc.
LAM-151-HT~LAM-251-HT
LAMINATING EPOXY
MECHANICAL PROPERTIES
89 90 87 86
Property Standard Units
200 F (93 C)
x 12 hrs
250 F (121 C)
x 8 hrs
140 F (60 C) x 2 hrs
+ 302 F (150 C)
x 4 hrs
87
16,600(114) 16,700(115) 16,300(112) 13,500(93) 13,500(93)
12,500(86) 10,800(74) 9,240(64) 9,690(67) 9,690(67)
4.75E+05(3.28)4.56E+05(3.14)4.14E+05(2.85)4.68E+05(3.23)4.28E+05(2.95)
5.5 3.9 3.8 4.2 5.6
(3.45)4.82E+05(3.32)
(105) 17,600(121) 18,100(125)
4.43E+05(3.05)4.10E+05(2.83)
21,400(148) 18,800(130) 15,200
THERMAL PROPERTIES
Property Standard Units
200 F (93 C)
x 12 hrs
3.84E+05(2.65)5.01E+05
250 F (121 C)
x 8 hrs
140 F (60 C) x 2 hrs
+ 302 F (150 C)
x 4 hrs
281 (138) 303 (151) 357 (181) 193 (90) 195 (91)
346 (175)
1
1 Hz, 3 C per minute.
2
Additional post cure may be required; contact Technical Department for details.
3
Store PRO-SET Epoxy resins and hardeners at room temperature in sealed containers until shortly before
use. As with many high-performance epoxy resins, repeated exposure to low temperatures during storage
may cause the resin to crystallize. If this occurs, warm the resin to 125 F and stir to dissolve crystals.
Hardeners may form carbamation when exposed to CO
2 and moisture in the atmosphere for extended periods
of time. Prevent carbamation by protecting hardeners from exposure until immediately prior to processing.
172 (78)
251 (122) 282 (139) 324 (162) 153 (67) 173 (78)
250 (121) 286 (141) 328 (164) 170 (77) 190 (88)
252 (122) 277 (136) 339 (171) 157 (69)